Preparation and properties of phosphoric acid doped sulfonated poly(tetra phenyl phthalazine ether sulfone) copolymers for high temperature proton exchange membrane application

Phosphoric acid-doped sulfonated poly(tetra phenyl phthalazine ether sulfone) (PA-SPTPPES) copolymers were successfully synthesized by the 4,4′-dihydroxydiphenylsulfone with 1,2-bis(4-fluorobenzoyl)-3,4,5,6- tetraphenylbenzene (BFBTPB) and 4,4′-difluorodiphenylsulfone in sulfolane. Poly(tetra phenyl phthalazine ether sulfone)s (PTPPESs) were prepared via an intramolecular ring-closure reaction of dibenzoylbenzene of precursor and hydrazine. The sulfonated poly(tetra phenyl phthalazine ether sulfone) (SPTPPES) membranes were obtained by sulfonation under concentrated sulfuric acid, and followed phosphoric acid-doped by immersion in phosphoric acid. Different contents of doped and sulfonated unit of PA-SPTPPES (10, 15, 20 mol% of BFBTPB) were studied by FT-IR, ¹H NMR spectroscopy, and thermo gravimetric analysis (TGA). The ion exchange capacity (IEC) and proton conductivity of SPTPPESs and PA-SPTPPESs were evaluated with increase of degree of sulfonation and doping level. The PA-SPTPPESs membranes exhibit proton conductivities (80 °C, relative humidity 30%) of 41.3 ∼ 74.1 mS/cm and the maximum power densities of PA-SPTPPES 10, 15, and 20 were about 294, 350, and 403 mW/cm ².